Applied Physics
Salah M. Abdul Aziz; Uday Muhsin Nayef; Mohammed Soham Rasheed
Abstract
Zinc oxide nanoparticles (ZnO NPs), copper oxide nanoparticles (CuO NPs) and CuO@ZnO NPs as a colloidal core-shell solution were synthesized by laser ablation. A Nd:YAG laser with an energy of 700 mJ, a wavelength of 1064 nm and 200 pulses was used for the ablation process. The colloidal solution was ...
Read More ...
Zinc oxide nanoparticles (ZnO NPs), copper oxide nanoparticles (CuO NPs) and CuO@ZnO NPs as a colloidal core-shell solution were synthesized by laser ablation. A Nd:YAG laser with an energy of 700 mJ, a wavelength of 1064 nm and 200 pulses was used for the ablation process. The colloidal solution was deposited on porous silicon (PSi) using the drop-casting method. The PSi substrates were prepared by photoelectrochemical etching (PECE) on n-type (111) silicon wafers. The study investigated the influence on the electrical, optical, morphological and structural properties of the CuO NPs and ZnO NPs samples when they were converted into a core-shell, specifically for their use in photodetector applications. XRD analysis revealed the presence of CuO, ZnO and CuO@ZnO by diffraction peaks at different angles. According to the SEM images, the nanoparticles show randomly distributed spherical grains, while PSi exhibits a sponge-like structure. The core-shell shape is confirmed by TEM images, which show a dark inner region consisting of CuO NPs and a much lighter outer region consisting of the ZnO nanoshell. The optical properties of the CuO@ZnO NPs were investigated and a minimum energy gap of 2.8 eV was found. The CuO@ZnO NPs/PSi/n-Si photodetector showed improved current-voltage (J-V) characteristics, rectifying properties and remarkable sensitivity in the visible to near-infrared region compared to other photodetector samples. The fabricated photodetector confirmed improved quantum performance, especially in the visible spectrum. The work aims to synthesize CuO@ZnO core-shell nanoparticles by a laser ablation technique to improve the electrical properties and spectral response of photodetectors.